Projekat
Naziv Project Name Voditelj
Istraživanja i razvoj metoda ispitivanja konstrukcija sa greškom u zavarima u funkciji ocjene vijeka eksploatacije Research and development of testing methods for constructions with fault in welded joins in order to define exploatation life Mehmed Behmen
Kljucne rijeci
Kljucne rijeci Keywords
konstrukcija construction
vijek trajanja life
zavareni spoj welded join
brzina rasta prsline speer of rapture propagation
  fatigue limit
Klasifikacija projekta
Rezime
Rezime Resume
Mehanička svojstva osnovnog materijala NIOMOL 490K u odnosu na pravac valjanja su dobro uravnotežena (R0.2, Rm) izuzev relativnog izduženja (A%) gdje uzorci iz podužnog pravca imaju bolja svojstva za cea 20%. Simulacioni procesi termičkog ciklusa zavarivanja na simulatoru «SMIDWELD» imaju stabilne karakteristike, pa su dobra osnova za izbor optimalnih tehnologija zavarivanja. Sa stanovišta mehanike loma (max. energija loma) u kritičnom dijelu zone uticaja toplote (ZUT) dobijeni su najpovoljniji parametri tehnologije zavarivanja. Energija loma materijala ZUT-a je direktno u funkciji temperature i vremena hlađenja Atg/5 U procesu analize uticaja postupka zavarivanja na mehaničke karakteristike zavara i ZUT-a, a za slučaj višeprolaznog zavarivanja, može se zaključiti: MAG postupak zavarivanja sa dodatnim materijalom VAC 60Ni (6 prolaza), daje slabije rezultate nego REL sa EVB 2.5NiMo (6 prolaza). Sklonost krtom lomu izražena je na nižim temperaturama za MAG postupak zavarivanja što ukazuje na slabe karakteristike dodatnog materijala. Obzirom na usvojenu geometriju epruvete za definisanje energije loma, greške tipa zajeda lica zavara i greške tipa neprovarenog korjena imale bi iste efekte u rezultatima analiza nukleacije i propagacije u strukturi zavara i ZUT-a. Preporučuje se u narednom ciklusu istraživanja proces utvrđivanja dinamičke moći nošenja zavara sa unutarnjom greškom, a za već definisane tehnologije zavarivanja na opserviranom materijalu NIOMOL 490K. Mechanical characteristics od the basic material NIOMOL 490K regarding the straight of rolling are relatively balanced (R0.2, Rm), except for relative elongation (A%) where samples from longitudinal straight have better characteristics for cea 20%. Simulation proceses of thermic cycle of vvelding on simulator «SMIDWELD» have stable characteristics, then they are good basis for selectioon of optimal vvelding technology. Considering mechanics of failure (max. Energy of failure) in critical part ofjieat influence zone, optimum parameters of vvelding technology are obtained. The energy of failure in the heat influence zone is directly in funetion of temperature and cooling time Atg/j In the process of analysis of the influence of vvelding method on join and heat influence zone mechanical characteristics, in the case of multipass vvelding, vve are able to conelude: MAG method of vvelding vvith added material VAC 60Ni (6 passes) imparts vvorse results than REL vvith EVB 2.5 NiMo (6 passes). Liability to brittle failure is more possible on less temperatures for MAG vvelding method vvhich point out on bad characteristics of added material. Regarding the defined sample geometry for defining the energy of failure, faults on the surface of the vvelded joint and ili made root vvould have the same effects in results of analysis of initial erack and erack progression in a joint strueture and heat influence zone. It is recomended in the next cycle of research defining of dinamical bearing povver of vvelded join vvith internal mistake for already defined technologies of vvelding on opservated material NIOMOL 490K.
1 - 1
Povezanost sa drugim projektima
Naziv projekta
Studij vijeka trajanja oštećenih zavarenih konstrukcija - mogućnost popravke i korištenja
1 - 1
Cijena projekta
Cijena
28982
Trajanje projekta
Pocetak Kraj
28.12.01 28.11.02
Izvori finansiranja
 
  Elektrotehnički fakultet Sarajevo i Akademija nauka i umjetnosti Bosne i Hercegovine   Copyright © 2006, All rights reserved.